AC Resistivity and Power Loss of Mn-Zn Ferrites

Seiichi YAMADA; Etsuo OTSUKI; Tsutomu OTSUKA

AC Resistivity and Power Loss of Mn-Zn Ferrites

Seiichi YAMADA, Etsuo OTSUKI, Tsutomu OTSUKA

Full Text Views

0

Share
Cite this

Summary :

Ac resistivity and power loss values for Mn-Zn ferrite material have been investigated by electrical and magnetic measurements. The ac resistivity shows an inductive dependency on frequency for the low dc resistive samples or for highly dc resistive ones at high temperature, while a capacitive dependency on frequency was observed for the highly resistive materials at the room temperature. These phenomena were interpreted by the dependence of ac resistivity on the dc resistivity, complex permeability and complex permittivity. The dependency of the power losses on the dc resistivity, temperature and frequence were also examined with analysis of power loss term. Dividing the power loss into hysteresis loss and eddy current loss, the frequency dependence of the eddy current loss was found to vary with the magnitude of the dc resistivity as follows: The eddy current loss of low dc resistive materials depends on the dc resistivity. On the other hand, the eddy current loss for high resistive materials is determined by the ac resistivity, contributed from dielectric loss.

Publication: IEICE TRANSACTIONS on Communications Vol.E75-B No.11 pp.1192-1198

Publication Date: 1992/11/25

Publicized

Online ISSN

DOI

Type of Manuscript: Special Section PAPER (Special Issue on Telecommunications Energy Systems and Switching Power Converters)

Category

Cite this

Copy

Seiichi YAMADA, Etsuo OTSUKI, Tsutomu OTSUKA, "AC Resistivity and Power Loss of Mn-Zn Ferrites" in IEICE TRANSACTIONS on Communications, vol. E75-B, no. 11, pp. 1192-1198, November 1992, doi: .
Abstract: Ac resistivity and power loss values for Mn-Zn ferrite material have been investigated by electrical and magnetic measurements. The ac resistivity shows an inductive dependency on frequency for the low dc resistive samples or for highly dc resistive ones at high temperature, while a capacitive dependency on frequency was observed for the highly resistive materials at the room temperature. These phenomena were interpreted by the dependence of ac resistivity on the dc resistivity, complex permeability and complex permittivity. The dependency of the power losses on the dc resistivity, temperature and frequence were also examined with analysis of power loss term. Dividing the power loss into hysteresis loss and eddy current loss, the frequency dependence of the eddy current loss was found to vary with the magnitude of the dc resistivity as follows: The eddy current loss of low dc resistive materials depends on the dc resistivity. On the other hand, the eddy current loss for high resistive materials is determined by the ac resistivity, contributed from dielectric loss.
URL: https://globals.ieice.org/en_transactions/communications/10.1587/e75-b_11_1192/_p

Copy

@ARTICLE{e75-b_11_1192,
author={Seiichi YAMADA, Etsuo OTSUKI, Tsutomu OTSUKA, },
journal={IEICE TRANSACTIONS on Communications},
title={AC Resistivity and Power Loss of Mn-Zn Ferrites},
year={1992},
volume={E75-B},
number={11},
pages={1192-1198},
abstract={Ac resistivity and power loss values for Mn-Zn ferrite material have been investigated by electrical and magnetic measurements. The ac resistivity shows an inductive dependency on frequency for the low dc resistive samples or for highly dc resistive ones at high temperature, while a capacitive dependency on frequency was observed for the highly resistive materials at the room temperature. These phenomena were interpreted by the dependence of ac resistivity on the dc resistivity, complex permeability and complex permittivity. The dependency of the power losses on the dc resistivity, temperature and frequence were also examined with analysis of power loss term. Dividing the power loss into hysteresis loss and eddy current loss, the frequency dependence of the eddy current loss was found to vary with the magnitude of the dc resistivity as follows: The eddy current loss of low dc resistive materials depends on the dc resistivity. On the other hand, the eddy current loss for high resistive materials is determined by the ac resistivity, contributed from dielectric loss.},
keywords={},
doi={},
ISSN={},
month={November},}

Copy

TY - JOUR
TI - AC Resistivity and Power Loss of Mn-Zn Ferrites
T2 - IEICE TRANSACTIONS on Communications
SP - 1192
EP - 1198
AU - Seiichi YAMADA
AU - Etsuo OTSUKI
AU - Tsutomu OTSUKA
PY - 1992
DO -
JO - IEICE TRANSACTIONS on Communications
SN -
VL - E75-B
IS - 11
JA - IEICE TRANSACTIONS on Communications
Y1 - November 1992
AB - Ac resistivity and power loss values for Mn-Zn ferrite material have been investigated by electrical and magnetic measurements. The ac resistivity shows an inductive dependency on frequency for the low dc resistive samples or for highly dc resistive ones at high temperature, while a capacitive dependency on frequency was observed for the highly resistive materials at the room temperature. These phenomena were interpreted by the dependence of ac resistivity on the dc resistivity, complex permeability and complex permittivity. The dependency of the power losses on the dc resistivity, temperature and frequence were also examined with analysis of power loss term. Dividing the power loss into hysteresis loss and eddy current loss, the frequency dependence of the eddy current loss was found to vary with the magnitude of the dc resistivity as follows: The eddy current loss of low dc resistive materials depends on the dc resistivity. On the other hand, the eddy current loss for high resistive materials is determined by the ac resistivity, contributed from dielectric loss.
ER -